SHK PPR-C PIPES & FITTINGS
Raw Material: Polypropylene Random Copolymer
SHK PPR-C Pipes and fittings are manufactured from Poly-Propylene Random Copolymer raw material which are the most efficient solution today for Hot & Cold Water Supply.
With Advantages of High Pressure Handling, Wide Temperature Operating Range and Smooth Surefaced material, Poly-Propylene Random Copolymer has become the most Recommended Pipes for Industrial as well as Domestic Usage.
Standards for SHK PPR-C Pipes & Fittings
(a) IS 15801 for PPR-C Pipe manufacturing Process
(b) DIN 8077-8078 for PPR-C Pipes General Quality Requirements and Testing
(c) DIN 16962 Pipe Joints
As per IS : 15801 & DIN 8077 Wall Thickness and Weight Corresponding to Different Pipe Sizes
| D | SDR 11/PN10 | SDR 7.4 / PN 16 | SDR 6 / PN 20 | |||
| Outerdiameter of pipe (mm) | S Thickness pipe in mm | Mass in kg/m | S Thickness in mm | Mass in kg/m | S Thickness in mm | Mass in kg/m |
| 20 | 1.9 | 0.107 | 2.8 | 0.148 | 3.4 | 0.172 |
| 25 | 2.3 | 0.164 | 3.5 | 0.230 | 4.2 | 0.266 |
| 32 | 2.9 | 0.261 | 4.4 | 0.370 | 5.4 | 0.434 |
| 40 | 3.7 | 0.412 | 5.5 | 0.575 | 6.7 | 0.671 |
| 50 | 4.6 | 0.638 | 6.9 | 0.896 | 8.3 | 1.040 |
| 63 | 5.8 | 1.01 | 8.6 | 1.410 | 10.5 | 1.650 |
| 75 | 6.8 | 1.41 | 10.3 | 2.010 | 12.5 | 2.340 |
| 90 | 8.2 | 2.03 | 12.3 | 2.870 | 15 | 3.360 |
| 110 | 10 | 3.01 | 15.1 | 4.300 | 18.3 | 5.010 |
| 160 | 14.6 | 6.38 | 21.9 | 9.040 | 26.6 | 10.60 |
Thermal Properties
Properties | Test Method | Unit | Value |
Thermal Conductivity at 23 C | DIN 52612 | W/mok | 0.23 |
Specific heat at 23 C | Calorimeter | Kj/kgok | 1.73 |
Coefficient of linear thermal expansion | DIN 53752 | K-1 | 1.5 x 10-4 |
Under weight deformation temperature 1.8 N/mm2 | ISO 306 | °C | 44 |
0.45 N/ mm2 | ISO 3146 | °C | 42 |
VICAT softening point | 0.095 | °C | 130 |
Mechanical Properties
Properties | Test Method | Unit | Value | |
Tensile Stress at Yield (50mm / minute) | ISO 527-1,2 | MPa | 24 | |
Tensile Stress at Yield (50mm / minute) | ISO 527-1,2 | % | 10 | |
Tensile modules (secant ) | ISO 527-1,2 | MPa | 850 | |
Flexural Modulus | ASTM D 790 | MPa | 850 | |
Tear Strength | ISO 527 | MPa | 40 | |
Elongation at tear | ISO 527 | % | 800 | |
Shore D Hardness | DIN 53 505 | – | 65 | |
Pipe Friction Factor | ISO 179/leA | – | 0.007 | |
CHARPY Impact Strength | 23°C | ISO 179/leA | KJ/m2 | 22 |
0°C | ISO 179/leA | KJ/m2 | 4.0 | |
-30°C | ISO 179/leA | KJ/m2 | 2.5 | |
CHARPY Impact Strength (unnotched) | 23°C | ISO 179/leA | KJ/m2 | No failure |
0°C | ISO 179/leA | KJ/m2 | No failure | |
-30°C | ISO 179/leA | KJ/m2 | 43 | |